Whether or not the final component develops porosity during drying depends on the amount of material that is dissolved in Stage I. If we assume that the total relative volume filled by the solid particles at the end of the process is w, then a dense component can only be obtained if the gel volume after drying is large enough to fill the remaining pores (1 − w). Under this assumption we deduce that a dense component can only be obtained if: