However, the diffraction peak intensity is slightly weaker for the as-cold-sintered and 300°C post-heat-treated samples, when compared with those post-heat-treated at higher temperatures over 400°C. After that, nearly no change in diffraction peaks is observed by further increasing the post-heat-treating temperature.