Honeycomb-like aligned carbon nanot

Honeycomb-like aligned carbon nanotube films were grown by pyrolysis of iron phthalocyanine. The patterned structure was characterized by a scanning electron micrograph (SEM) and an atomic force micrograph (AFM). Wettability studies revealed the film surface showed a super-hydrophobic property with much higher contact angle (163.4 ± 1.4°) and lower sliding angle (less than 5°)a water droplet moved easily on the surface. In contrast to a densely packed aligned carbon nanotube, the sliding feature was strongly affected by microstructure of surface.

0/5000

源语言: -

目标语言: -

结果 (简体中文) 1: [复制]

复制成功！

通过热裂解酞菁铁来生长蜂窝状排列的碳纳米管薄膜。通过扫描电子显微镜（SEM）和原子力显微镜（AFM）表征图案化的结构。润湿性研究表明，薄膜表面显示出超疏水性，其接触角（163.4±1.4°）高得多，滑动角低（小于5°），水滴易于在表面上移动。与密集排列的定向碳纳米管相反，滑动特征受表面微观结构的强烈影响。

正在翻译中..

结果 (简体中文) 2:[复制]

复制成功！

蜂巢状的对齐碳纳米管薄膜由铁性邻苯二甲酰胺的热解生长。图案结构的特点是扫描电子显微图（SEM）和原子力显微图（AFM）。湿润性研究表明，薄膜表面具有超疏水性，接触角度更高（163.4 ± 1.4°），滑动角度较低（小于 5°），水滴在表面上轻松移动。与密集包装的对齐碳纳米管相比，滑动特征受到表面微观结构的强烈影响。

正在翻译中..

结果 (简体中文) 3:[复制]

复制成功！

以酞菁铁为原料，采用热分解法制备了蜂窝状排列的碳纳米管薄膜。用扫描电子显微镜（SEM）和原子力显微镜（AFM）对其结构进行了表征。润湿性研究表明，薄膜表面具有超疏水性，接触角（163.4±1.4°）大，滑动角（小于5°）小。与密集排列的碳纳米管相比，表面的微观结构对碳纳米管的滑动特性有很大的影响。<br>

正在翻译中..

其它语言

本翻译工具支持: 世界语, 丹麦语, 乌克兰语, 乌兹别克语, 乌尔都语, 亚美尼亚语, 伊博语, 俄语, 保加利亚语, 信德语, 修纳语, 僧伽罗语, 克林贡语, 克罗地亚语, 冰岛语, 加利西亚语, 加泰罗尼亚语, 匈牙利语, 南非祖鲁语, 南非科萨语, 卡纳达语, 卢旺达语, 卢森堡语, 印地语, 印尼巽他语, 印尼爪哇语, 印尼语, 古吉拉特语, 吉尔吉斯语, 哈萨克语, 土库曼语, 土耳其语, 塔吉克语, 塞尔维亚语, 塞索托语, 夏威夷语, 奥利亚语, 威尔士语, 孟加拉语, 宿务语, 尼泊尔语, 巴斯克语, 布尔语(南非荷兰语), 希伯来语, 希腊语, 库尔德语, 弗里西语, 德语, 意大利语, 意第绪语, 拉丁语, 拉脱维亚语, 挪威语, 捷克语, 斯洛伐克语, 斯洛文尼亚语, 斯瓦希里语, 旁遮普语, 日语, 普什图语, 格鲁吉亚语, 毛利语, 法语, 波兰语, 波斯尼亚语, 波斯语, 泰卢固语, 泰米尔语, 泰语, 海地克里奥尔语, 爱尔兰语, 爱沙尼亚语, 瑞典语, 白俄罗斯语, 科西嘉语, 立陶宛语, 简体中文, 索马里语, 繁体中文, 约鲁巴语, 维吾尔语, 缅甸语, 罗马尼亚语, 老挝语, 自动识别, 芬兰语, 苏格兰盖尔语, 苗语, 英语, 荷兰语, 菲律宾语, 萨摩亚语, 葡萄牙语, 蒙古语, 西班牙语, 豪萨语, 越南语, 阿塞拜疆语, 阿姆哈拉语, 阿尔巴尼亚语, 阿拉伯语, 鞑靼语, 韩语, 马其顿语, 马尔加什语, 马拉地语, 马拉雅拉姆语, 马来语, 马耳他语, 高棉语, 齐切瓦语, 等语言的翻译.