The incorporation of Ti ions into the framework generates both acidic hydroxyl groups and Lewis acid sites in TS-1. The acidic hydroxyl groups with a moderate acidity is originated from the internal Si–OH groups adjacent to the ‘‘open” Ti sites, while the Lewis acidity is due to the framework Ti ions. It is the internal silanols in TS-1 that contribute to the condensation of EDA rather than its Lewis acid sites.