A typical microstructure of the ceramics of the second group is shown in Fig. 6. As a consequence of the number of pores in this material and the resulting incomplete grain-to-grain contacts the electrical properties of the ceramics are poor. The electrical resistivity at room temperature is in the range of some k cm to M cm which is high compared to the few cm required for practical applications [13].