we confirm this speculation,showing that oxide-passivated pyramidal textured silicon has a higher density of interface states than can be accounted for by surface area and orientation, and that the additional defects are predominantly acceptorlike when above, or donorlike when below, an energy of 0.3 eV higher than the valence band.