Prior to analyses, Raman spectra of both cold and hydrothermally sintered samples were normalized with the asymmetric LO multiphonon peak located at 1155 cm−1 as reference (Fig. 5). No significant changes are observed, except for the peaks located at 938, 1426 and 2935 cm−1, respectively attributed to CeC, CeO and CH3 symmetric stretching.