The effect of hydrogen on mechanical properties starts to manifest itself even when its content is (1 . 2)x m3/kg. (Carbon steel C45e contains approximately 3x m3kg which proportionally decreases metal plasticity and failure resistance. At a hydrogen content (8 . 10)~10-~ m3kg the steel failure becomes brittle, i. e.