从图1可见，虽然三个样品都是旋涂一层的纳米银线，但是随着纳米银线直径减

It can be seen from Figure 1 that although the three samples are all spin-coated nano-silver wires, as the diameter of the nano-silver wires decreases, the deposited layer of the nano-silver wires becomes thicker, especially when the nano-silver wires with a diameter of 20 nm are deposited. A dense deposition layer of silver nanowires can be seen in the samples of the shaped silver nanowires.

It can be seen from Figure 1 that although the three samples are spin coated with a layer of nano silver wire, the nano silver wire deposition layer is significantly thickened as the diameter of the nano silver wire decreases, especially in the nano silver wire film sample with a diameter of 20 nm.

As can be seen from Figure 1, although all three samples are coated with a layer of nano-silver wires, with the decrease of the diameter of nano-silver wires, the nano-silver wire deposition layer is obviously thickened, especially in the nano-silver wire deposition-shaped nano-silver wire film samples with a diameter of 20 nm, the nano-silver wire dense deposition layer can be seen.