The initial dissolution of nano-alumina leads a higher ettringite content at the very early hydration stage, however, the dissolution of nano-alumina may also be controlled by S species in pore solutionduring the induction period. The dissolution of nano-alumina removes aqueous S species from pore solution and speeds up the consumption of gypsum significantly, thus promoting the hydration of C3A