Fig. 2 Schematic of the reactive cold sintering process. The pressure falls as the particles rearrange and compact under load. As the temperature is increased there is further densification through removal of the transient liquid phase causing the pellet to further decrease in thickness . Under the additional thermal treatment there is the reactive transformation to a single phase SrTiO3 ceramic.