G5 powder (100% anatase, s.s.a. = 370 m2/g) was previously compacted by uniaxially pressing the powder at 120 MPa and 500 MPa.The trend of the curves of the samples of G5, subjected to heating up to 700 °C, is shown in Fig. 5a. The curves obtained from G5 samples pressed at 120 MPa and 500 MPa have similar trends. However, the influence of the pressure can be noticed: due to the greater rearrangement of less packed particles, G5 pressed at 120 MPa initially shrank more in the temperature range from 20 to about 580 °C, temperature above which the slope of the curve of the sample pressed at 500 MPa became more marked. At 700 °C, the samples pressed at 120 MPa and 500 MPa had a total shrinkage of ˜8% and ˜9% respectively, resulting in a slightly greater final contraction of the sample G5-500 MPa.
0/5000
源语言: -
目标语言: -
结果 (简体中文) 1: [复制]
复制成功!
预先在120 MPa和500 MPa下单轴压制G5粉末(100%锐钛矿,ssa = 370 m2 / g),加热到700°C时G5样品的曲线趋势为如图5a所示。从分别在120 MPa和500 MPa下压制的G5样品获得的曲线具有相似的趋势。但是,可以注意到压力的影响:由于较小堆积颗粒的较大重排,以120 MPa压制的G5最初在20至580°C的温度范围内收缩更多,在此温度下曲线的斜率大于在500 MPa下加压的样品变得更加明显。在700°C下,分别在120 MPa和500 MPa下压制的样品的总收缩率分别约为8%和9%,从而导致样品G5-500 MPa的最终收缩稍大。
正在翻译中..
结果 (简体中文) 2:[复制]
复制成功!
G5 powder (100% anatase, s.s.a. = 370 m2/g) was previously compacted by uniaxially pressing the powder at 120 MPa and 500 MPa.The trend of the curves of the samples of G5, subjected to heating up to 700 °C, is shown in Fig. 5a. The curves obtained from G5 samples pressed at 120 MPa and 500 MPa have similar trends. However, the influence of the pressure can be noticed: due to the greater rearrangement of less packed particles, G5 pressed at 120 MPa initially shrank more in the temperature range from 20 to about 580 °C, temperature above which the slope of the curve of the sample pressed at 500 MPa became more marked. At 700 °C, the samples pressed at 120 MPa and 500 MPa had a total shrinkage of ˜8% and ˜9% respectively, resulting in a slightly greater final contraction of the sample G5-500 MPa.
正在翻译中..
结果 (简体中文) 3:[复制]
复制成功!
G5粉末(100%锐钛矿,s.s.a.=370m2/g)先前通过在120mpa和500mpa下单轴挤压粉末来压实。G5样品在700℃下加热后的曲线趋势如图5a所示。从120mpa和500mpa压力下的G5样品获得的曲线具有相似的趋势。然而,压力的影响是可以注意到的:由于较小填充颗粒的较大重排,在120mpa压力下的G5在20-580℃范围内开始收缩更多,高于此温度时,在500mpa压力下的试样曲线斜率变得更明显。在700°C下,在120兆帕和500兆帕压力下压制的试样的总收缩率分别为8%和9%,导致试样G5-500兆帕的最终收缩率稍大。
正在翻译中..
 
其它语言
本翻译工具支持: 世界语, 丹麦语, 乌克兰语, 乌兹别克语, 乌尔都语, 亚美尼亚语, 伊博语, 俄语, 保加利亚语, 信德语, 修纳语, 僧伽罗语, 克林贡语, 克罗地亚语, 冰岛语, 加利西亚语, 加泰罗尼亚语, 匈牙利语, 南非祖鲁语, 南非科萨语, 卡纳达语, 卢旺达语, 卢森堡语, 印地语, 印尼巽他语, 印尼爪哇语, 印尼语, 古吉拉特语, 吉尔吉斯语, 哈萨克语, 土库曼语, 土耳其语, 塔吉克语, 塞尔维亚语, 塞索托语, 夏威夷语, 奥利亚语, 威尔士语, 孟加拉语, 宿务语, 尼泊尔语, 巴斯克语, 布尔语(南非荷兰语), 希伯来语, 希腊语, 库尔德语, 弗里西语, 德语, 意大利语, 意第绪语, 拉丁语, 拉脱维亚语, 挪威语, 捷克语, 斯洛伐克语, 斯洛文尼亚语, 斯瓦希里语, 旁遮普语, 日语, 普什图语, 格鲁吉亚语, 毛利语, 法语, 波兰语, 波斯尼亚语, 波斯语, 泰卢固语, 泰米尔语, 泰语, 海地克里奥尔语, 爱尔兰语, 爱沙尼亚语, 瑞典语, 白俄罗斯语, 科西嘉语, 立陶宛语, 简体中文, 索马里语, 繁体中文, 约鲁巴语, 维吾尔语, 缅甸语, 罗马尼亚语, 老挝语, 自动识别, 芬兰语, 苏格兰盖尔语, 苗语, 英语, 荷兰语, 菲律宾语, 萨摩亚语, 葡萄牙语, 蒙古语, 西班牙语, 豪萨语, 越南语, 阿塞拜疆语, 阿姆哈拉语, 阿尔巴尼亚语, 阿拉伯语, 鞑靼语, 韩语, 马其顿语, 马尔加什语, 马拉地语, 马拉雅拉姆语, 马来语, 马耳他语, 高棉语, 齐切瓦语, 等语言的翻译.

Copyright ©2024 I Love Translation. All reserved.

E-mail: