The as-compacted green samples were placed onto an uncovered corundum plate after being baked for 12 h at 200°C and then sintered in a furnace at a temperature ranging between 400°C and 950°C for 4 h at a heating rate of 2°C/min. The corresponding green pellets and ceramics were denoted as CSP180 and LMT400-950, respectively.