This is an important advantageous feature of the cold sintering process, since large grain sizes have a deleterious effect on the mechanical strength of brittle materials32. We also observed that the metastable vaterite phase is preserved after pressing at 500 MPa and does not present a preferential crystallographic orientation, even at high pressures (Supplementary Fig. 1).