综上所述，为获得力学性能优异的纤维将采取以下两步骤。第一，初生纤维的制

In summary, the following two steps will be taken to obtain fibers with excellent mechanical properties. First, the preparation of the nascent fiber: the spinning solution with a concentration of 11.7% is squeezed into a coagulation bath at a rate of 0.05 mm/s at a rate of 0.05 mm/s, and coagulated, and then drawn and dried at a rate of 2 rap/s by a winding roller That is, nascent fiber.

你已超过允许的翻译次数。请稍后再试。

To sum up, the following two steps will be taken to obtain fibers with excellent mechanical properties. First, the preparation of primary fiber: the spinning solution with concentration of 11.7% was extruded into the coagulation bath at 20 ℃ at the rate of 0.05mm/s, and then the primary fiber was drawn and dried at the rate of 2 rap / s of the winding roller.