However, diffraction peaks corresponding to the metastableM2C carbide and g-Fe were not observed in the as-HIP sample or inthe samples treated by conventional quenching and tripletempering treatment.
However, diffraction peaks corresponding to the metastable<br>M2C carbide and g-Fe were not observed in the as-HIP sample or in<br>the samples treated by conventional quenching and triple<br>tempering treatment.