However, these impurity phases were not stable at high temperatures, such that they could be removed [27,28]. The Mg(OH)2 and Li2TiO3 contents decreased as the sintering temperature increased (Fig. 3(B) and Table 1), with these disappearing at 600°C, as indicated by the TG/ DTA results in Fig. 2.