6005A的材质侧顶型材供应商第5次试模，还是不合格，而且由于短时间多

The 6005A material side roof profile supplier's 5th mold test was still unqualified, and due to the short-term and multiple-frequency mold test, the mold has been cracked and scrapped (the specific mold damage photo is below). <br>Due to the current shutdown of the supplier's mold factory and related heat treatment equipment, new molds cannot be re-invested before February 14. <br><br>Based on the above situation, the A5.1 version plan can no longer be satisfied. The attachment is the first train development plan estimated based on the current situation, please refer to. <br><br>Sorry for this issue and hope you can understand our difficulties, thank you.

The 5th mold test of 6005A side top profile supplier is still unqualified, and the mold has been cracked and scrapped due to short-time and frequent machine mold test (see the photo below for specific mold damage).<br>At present, the supplier's mold factory and relevant heat treatment equipment have been shut down, so it is impossible to put a new mold into operation before February 14.<br>Based on the above, a5 The version 1 plan can not be met. The appendix is the first train development plan estimated based on the current situation. Please refer to it.<br>We apologize for this problem and hope you can understand our difficulties. Thank you.

The supplier of the material side top profile of 6005A failed the fifth mold test, and the mold was cracked and scrapped due to the short time and multiple times of mold test on the machine (below the specific mold damage photo). At present, as the supplier's mold factory and related heat treatment equipment have been shut down, no new mold can be put in before February 14th. In view of the above situation, the A5.1 version plan can no longer be met. The attachment is the first train development plan estimated based on the current situation. Please refer to it. I apologize for this problem and hope you can understand our difficulties. Thank you.