The SiO2 content after acid activation increased from 39.1% to 75.8%, while the Al2O3 content decreased from 35.9% to 18.9%. For GY-FA, the SiO2 content after acid activation enhanced from 51.6% to 58%, while the Al2O3 content decreased from 30.4% to 30.3%.