实验结果表明，以1%的SDS作为乳化体系，m（芯材）:m（壁材）=2:

The experimental results show that with 1% SDS as the emulsification system, m (core material): m (wall material) = 2:10, at 20. After stirring at 400-500 rpm for 12 h under C condition, microcapsules with ideal morphology with smooth surface, uniform particles and complete coating film can be obtained, and the average particle size is 35.82 μm.

The experimental results show that with 1% SDS as the emulsion system, m (core material): m (wall material) = 2:10, at 20. After stirring at the rate of 400-500 rpm for 12 hours under the condition of C, microcapsules with ideal morphology with smooth surface, uniform particles and complete coating film can be obtained, and the average particle size is 35.82 μ m。

The experimental results showed that 1% SDS was used as emulsion system, and the ratio of m (core material): m (wall material) was 2: 10, which was between 20. Under the condition of C, after stirring at the rate of 400-500 rpm for 12 hours, microcapsules with smooth surface, uniform particles and complete coating film can be obtained, and the average particle size is 35.82 μm m.