This may be because the appearance of the "protective layer" of brucite restricts the leakage of OH-, resulting in a highly alkaline corrosion product.
Perhaps this is because the appearance of brucite "protective layer" limits the leakage of OH-, resulting in high alkalinity of the generated corrosion products.