Although the Tb content of the surface layer (within 500 µm) in Tb 70 Cu 30 diffused magnet was higher compared to Tb-Y-La-Cu diffused magnet, their contribution to the overall coercivity is about the same, since the magnetically hardened Tb-rich shells of 14 nm is already saturated for the magnetic hardening effect [13]