For the oxide region, a 60-nm-thick layer was deposited on a p-type (100)-oriented silicon substrate by means of a 4-inch radiofrequency magnetron sputtering system from a pure ZnO target, using a power density value of 0.97 W cm,a 15 lbar Ar pressure, and a substrate temperature of 400 C.