Consequently, the dislocation/solute interaction energy typically consists of size misfit and more specific chemical core contributions, where the former results from the interaction of the volumetric strain field around the solute with the elastic stress field of the dislocation and the latter is caused by the different bonding environment withinthe nonlinear core and stacking fault regions of the dislocations