Similar results have been calculated (not shown) to show that Al casting alloys A535 and A710 both have a significantly higher |dT/d(fS1/2)| near (fS)1/2 = 1.0 than A356, thus predicting the significantly higher crack susceptibility of these alloys than A356. This prediction is consistent with the known high crack susceptibility of A535 and A710