• Thank you for the 5 cycle spring force testing MSOP. Since the equipment use 1 measurement program that complete 5 strokes, is there raw and graph data that can be shared from one the test sample? Item 2: • The detail cross section of the spring from VP, appear to have a smaller round at the edge of the spring. If Fitbit team want to target a round in the 0.02mm-0.04mm range, what update (design or process) would VP recommend to achieve desired design range?• Please explain, in detail, what tooling change would have to be done.• Please share any risk impact to other areas of the spring. Would update affect bends and angles on the spring arm?Item 3:• Hardness values are in line with what is expected. Can VP confirm the raw beryllium copper stock is full hard (TM04)?