A layer-by-layer N-doped graphene/MoS2/N-doped graphene stacking heterostructure prepared by an in situ thermal decomposition–reduction method showed an excellent cycling stability with a high specific capacity of 552 mA h g−1 at 1 A g−1 after 600 cycles for LIBs.