The compressive strength of mortar specimens curing at low humidity and low-humidity environment test pieces were higher than the standard 14 days curing. This may be due to the standard curing specimens containing excess water.
The pressure strength of the mortar test piece smaintained in low wet and low humidity environment was higher than that of the standard maintenance 14-day test. This may be due to excessive water in standard maintenance test sits.
The compressive strength of mortar specimens cured in low humidity and low pressure and low humidity was higher than that of standard specimens cured for 14 days. This may be due to excessive water in standard curing specimens.<br>