CS of a covalently bonded (within the S–Mo–S layers) MoS2/graphite composite for use as a high capacity Li-Ion electrode was demonstrated, with fabrication of highly dense electrochemically active MoS2/graphite composites achieved with a relative density of 88%, using processing conditions of 140℃, 520 MPa for 60 min [72].